A Crosslinking Agent Modification Method for XLPE Bilayer Interface Mechanical Strength Enhancement
编号：127 访问权限：仅限参会人 更新：2024-08-26 13:04:56 浏览：189次 张贴报告

报告开始：暂无开始时间（Asia/Shanghai）

报告时间：暂无持续时间

所在会场：[暂无会议] [暂无会议段]

演示文件

提示：该报告下的文件权限为仅限参会人，您尚未登录，暂时无法查看。

摘要
Cable factory joints play a key role in XLPE submarine cable system. Nevertheless，XLPE interface has the lowest mechanical strength in the insulation layer, which will lead to the insulation crack or pore defects formation, even breakdown faults. In this work, a crosslinking agent modification method for XLPE bilayer interface mechanical strength enhancement was studied on both tablet compressing samples and real factory joints. The results show that crosslinking agent modification have the effect on XLPE interfacial mechanical strength enhancement and reduce pore defects formation.
 
关键词
cable joint,offshore wind power,power transmission,submarine cable,XLPE
报告人
Yang Lv
R&D engineer Beijing Institute of Smart Energy

稿件作者
Yang Lv Beijing Institute of Smart Energy
Li Yin Beijing Institute of Smart Energy
发表评论
验证码 看不清楚，更换一张
全部评论
重要日期

  • 会议日期

    11月06日

    2024

    至

    11月08日

    2024

  • 09月15日 2024

    初稿截稿日期

  • 11月08日 2024

    注册截止日期

主办单位
Huazhong University of Science and Technology
联系方式
登录查看完整联系方式
历届会议
移动端
在手机上打开
小程序
打开微信小程序
客服
扫码或点此咨询